Study of High Temperature Synthetic Polymer Fracturing Fluid
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    根据高温低渗储层压裂改造对压裂液性能的要求,从聚合物分子结构分析入手,以聚丙烯酰胺、聚丙烯酸、2.丙烯酰胺基。2.甲基丙磺酸(AMPS)为单体,合成新型耐高温聚合物,并对其性能进行了评价。实验结果表明,剪切3h后,压裂液黏度降低1.4mPa·s,剪切稳定性良好,并且剪切恢复性较好。随着温度的增加,压裂液交联时间逐渐缩短。该压裂液耐温可达170℃。在60℃时,聚合物压裂液破胶困难,可以通过提高破胶剂加量以提高压裂液破胶效果。聚合物压裂液的残渣率为0.83%,对岩心的伤害率为16.7%,对支撑裂缝导流能力的伤害小于植物胶压裂液。适合高温低渗储层的压裂改造。图5表3参2

    Abstract:

    According to the requirement of high-temperature low permeability reservoir hydraulic fracturing treatment to the propriety of fracturing fluid,a novel high temperature polymer was synthesized by polyacrylic acid,polyacrylamide,2-acrylamido-2-methylpropanesulfonic acid(AMPS).Performance evaluation experiment results showed that the viscosity of fracturing fluid decreased by 1.4 mPa · s after shearing 3 hrs,which possessed good shear stability and viscosity recovery propriety.The crosslinking time gradually decreased with increasing temperature.The temperature resistance of fracturing fluid reached to 170℃.The fracturing fluid was difficult to break at 60℃,which could be overcome through increasing the dosage of gel breaker.The residue of polymer fracturing fluid was of 0.83%,and the damage to core matrix was only 16.7%.The damage to propped fracture was far less than guar gum fracturing fluid which was fit for the stimulation of high-temperature low permeability reservoir.

    参考文献
    相似文献
    引证文献
引用本文

何春明,陈红军,刘超,卢智慧.高温合成聚合物压裂液体系研究[J].油田化学,2012,29(1):65-68.
HE Chun-Ming, CHEN Hong-Jun, LIU Chao, LU Zhi-Hui. Study of High Temperature Synthetic Polymer Fracturing Fluid[J]. OILFIELD CHEMISTRY,2012,29(1):65-68.

复制
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2013-04-16
  • 出版日期:
点击这里给我发消息

点击这里给我发消息